热氧化稳定性试验箱满足ASTM-D3012使用炉内样品旋转器测定丙烯塑料热氧化稳

日期:2018-11-15  179人浏览
放大字体  缩小字体
 热氧化稳定性试验箱满足ASTM-D3012使用炉内样品旋转器测定丙烯塑料热氧化稳定性的标准试验方法
QQ图片20181115110421
适用范围

5.1x00a0;Under the severe conditions of this test method, the specimens undergo degradation at a rate that is dependent upon the thermal endurance of the polypropylene material under examination.

5.2x00a0;The thermal level of this test method is considered sufficiently severe to cause failure of commercial grades of heat-stable polypropylene within a reasonable period of time. If desired, lower temperatures can be applied to estimate the performance of polypropylene materials with lower heat stability.

5.3x00a0;The technique of specimen rotation described in this test method provides an estimate of the life-temperature relationship of polypropylene. If this test method is conducted at different temperatures on the same material, a more reliable estimate of the life-temperature relationship of polypropylene is determined. This test method can be conducted at several temperatures and the data interpreted through use of the Arrhenius relation, by plotting the logarithms of times to failure against the reciprocals of the temperatures in kelvins (K). Temperatures in the range from 100 to 150x00b0;C, with intervals of 10x00b0;C, are suggested for this purpose.

5.4x00a0;The stability as determined under the prescribed test method is not directly related to the suitability of the compound for a use where different conditions prevail.

5.5x00a0;The specimen rotation technique of thermal aging increases the probability that all specimens will be exposed similarly and that the effect of temperature gradients in an oven will be minimized.

1.1x00a0;This test method provides a means for estimating the resistance of polypropylene, in molded form, to accelerated aging by heat in the presence of air using a forced draft oven.

1.2x00a0;The stability determined by this test method is not directly related to the suitability of the material for use when different environmental conditions prevail and shall not be used to predict performance.

Note 1x2014;The specified thermal levels in this test method are considered sufficiently severe to cause failure of commercial grades of heat-stable polypropylene within a reasonable period of time. If desired, lower temperatures can be applied to estimate the performance of polypropylene with lower heat stabilities.

1.3x00a0;The values stated in SI units are to be regarded as the standard. The values in parentheses are for information only.

1.4x00a0; This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Note 2x2014;This test method and ISO 4577x2013;1983 are technically similar but different in preparation of test specimens, thickness of test specimen, measurement of the number of air flow changes in the ovens, and the number of air changes per hour required.......
 
 
[ 新闻资讯搜索 ]  [ 加入收藏 ]  [ 告诉好友 ]  [ 打印本文 ]  [ 关闭窗口 ]

本文位置:新闻资讯
注:苏州亚诺天下仪器有限公司专业从事试验室品管检测设备研发生产30余年,有相对丰富的经验、有实力强大的团队、有超强的生产管理能力,选购试验室检测设备首选苏州亚诺天下仪器。我们愿竭诚为您服务0512-68559199,您的满意是我最大的追求。
参与评论
©2000-2019 亚诺天下™   乐赢彩票www.run-mate.com版权所有苏ICP备11049648号-14 首页 | 关于我们 | 总经理致辞 | 联系方式 | 企业荣誉 | 企业文化 | 服务支援 | 成功案例 | 人才战略 |